Descriptions
Refrax PROmor
特徴
・高密度耐火モルタル
・T-Clip® System・45° System・Belly Brick System に使用可能
| Property | Value | |
| Typical Chemical Analysis | SiC | 85.0 % |
| Al2O3 | 6.0 % | |
| P2O5 | 6.0 % | |
| Na2O+CaO | 1.5 % | |
| Bulk Density | 2.10 g/cm3 | |
| Cold Crushing Strenght | after drying at 110℃ | 35 MPa |
| after firing at 800℃ | 72 MPa | |
| after firing at 1,000℃ | 126 MPa | |
| Thermal Conductivity | at 400 - 1,000℃ | 3 - 6 W/mK |
| Maximum grain size | 1.0 mm | |
| Maximum service temperature | 1,250 ℃ | |
Refrax PLUSflow
特徴
・高密度耐火セルフフローキャスタブル
・T-Clip® System に使用可能
| Property | Value | |
| Typical Chemical Analysis | SiC | 70.4 % |
| Al2O3 | 21.0 % | |
| SiO2 | 6.0 % | |
| Fe2O3 | 0.5 % | |
| CaO | 1.6 % | |
| Others | 0.5 % | |
| Bulk Density | 2.67 g/cm3 | |
| Cold Crushing Strenght | after drying at 110℃ | 35 MPa |
| after firing at 800℃ | 72 MPa | |
| after firing at 1,000℃ | 126 MPa | |
| Thermal Conductivity | after firing at 500℃ | 7.2 W/mK |
| after firing at 1,000℃ | 5.7 W/mK | |
| Maximum grain size | 3 mm | |
| Maximum service temperature | 1,400 ℃ | |